17-7PH Sheet Stainless Steel SUS631 Cold Rolled Steel Strip In Coil
17-7PH Precipitation Hardening Alloy (UNS S17700) is a chromium-nickel-aluminum precipitation
hardening stainless steel used for applications requiring high strength and a moderate level of corrosion resistance.
| AISI, UNS |
EN, DIN |
JIS |
Chemical composition % |
| AISI 631, S17700 |
1.4568
X7CrNiAl17-7
|
SUS631 |
C 0.09, Si 1.00, Mn 1.00, Cr 16.0~18.0, Al 0.75~1.5,
NI 6.5~7.75
|
The 631 stainless alloy has been available for many years and has found application in aerospace
and many spring type applications requiring high strength.
17-7PH precipitation hardening alloy may be formed in a soft austenitic condition and hardened to
a high strength level by low temperature heat treatments.
The low temperature allows minimum distortion compared to conventional quench and temper
hardening processes. In addition to material produced by the standard refining procedures,
material which has been vacuum arc or electroslag remelted is available for further increase
in resistance to fatigue,for those applications subject to cyclic stresses.
PRODUCT FORMS
17-7PH precipitation hardening alloy is furnished as cut lengths plate, sheet and strip, coil.
In all forms, the material is furnished in the solution annealed condition.
In strip form, the material may be provided in a cold rolled condition suitable for
direct precipitation hardening heat treatment at 900°F (482°C).
followed by JIS G4305, JIS G4313, ASTM A693, ASTM F899, DIN EN 10088-2
For Details, please Contact
WUXI GUANGLU Special Steel Co., Ltd.
Stainless martensitic • precipitation hardening steel • stainless ferritic — Our answer to your needs
Tel: +86 510 81812873
Email: export@guanglusteel.com
Pesan Anda harus antara 20-3.000 karakter!